Dental Ceramics: Part I – An Overview of Composition, Structure and Properties

P. Jithendra Babu, Rama Krishna Alla, Venkata Ramaraju Alluri, Srinivasa Raju Datla, Anusha Konakanchi

  Open Access OPEN ACCESS  Peer Reviewed PEER-REVIEWED

Dental Ceramics: Part I – An Overview of Composition, Structure and Properties

P. Jithendra Babu1, Rama Krishna Alla2,, Venkata Ramaraju Alluri1, Srinivasa Raju Datla1, Anusha Konakanchi3

1Department of Prosthodontics, Vishnu Dental College, Bhimavaram, West Godavari, Andhra Pradesh, India

2Department of Dental Materials, Vishnu Dental College, Bhimavaram, West Godavari, Andhra Pradesh, India

3Department of Chemistry, Sasi Merit School, Bhimavaram, West Godavari, Andhra Pradesh, India

Abstract

Over the last decade, it has been observed that there is an increasing interest in the ceramic materials in dentistry. Esthetically these materials are preferred alternatives to the traditional materials in order to meet the patients’ demands for improved esthetics. Dental ceramics are usually composed of nonmetallic, inorganic structures primarily containing compounds of oxygen with one or more metallic or semi-metallic elements. Ceramics are used for making crowns, bridges, artificial denture teeth, and implants. The use of conservative ceramic inlay preparations, veneering porcelains is increasing, along with all-ceramic complete crown preparations. This article is a review of dental ceramics; divided into two parts such as part I and II. Part I reviews the composition, structure and properties of dental ceramics from the literature available in PUBMED and other sources from the past 50 years. Part II reviews the developments in evolution of all ceramic systems over the last decade and considers the state of the art in several extended materials and material properties.

At a glance: Figures

Cite this article:

  • Babu, P. Jithendra, et al. "Dental Ceramics: Part I – An Overview of Composition, Structure and Properties." American Journal of Materials Engineering and Technology 3.1 (2015): 13-18.
  • Babu, P. J. , Alla, R. K. , Alluri, V. R. , Datla, S. R. , & Konakanchi, A. (2015). Dental Ceramics: Part I – An Overview of Composition, Structure and Properties. American Journal of Materials Engineering and Technology, 3(1), 13-18.
  • Babu, P. Jithendra, Rama Krishna Alla, Venkata Ramaraju Alluri, Srinivasa Raju Datla, and Anusha Konakanchi. "Dental Ceramics: Part I – An Overview of Composition, Structure and Properties." American Journal of Materials Engineering and Technology 3, no. 1 (2015): 13-18.

Import into BibTeX Import into EndNote Import into RefMan Import into RefWorks

1. Introduction

In dentistry, ceramics represents one of the four major classes of materials used for the reconstruction of decayed, damaged or missing teeth. Other three classes are metals, polymers, and composites. The word Ceramic is derived from the Greek word “keramos”, which literally means ‘burnt stuff’, but which has come to mean more specifically a material produced by burning or firing [1]. A ceramic is an earthly material usually of silicate nature and may be defined as a combination of one or more metals with a non-metallic element usually oxygen. The American Ceramic Society had defined ceramics as inorganic, non-metallic materials, which are typically crystalline in nature, and are compounds formed between metallic and nonmetallic elements such as aluminum & oxygen (alumina - Al2O3), calcium & oxygen (calcia - CaO), silicon & nitrogen (nitride- Si3N4) [2]. Ceramics are characterized by their refractory nature, hardness, chemical inertness, biocompatibility [3, 4, 5] and susceptibility to brittle fracture [6, 7]. Ceramics are used for pottery, porcelain glasses, refractory material, abrasives, heat shields in space shuttle, brake discs of sports cars, and spherical heads of artificial hip joints [1, 8]. In dentistry, ceramics are widely used for making artificial denture teeth, crowns, bridges, ceramic posts, abutments, and implants and veneers over metal substructures [1, 9]. This article in part I; reviews the composition, structure and properties of dental ceramics from the literature available in PUBMED and other sources from the past 50 years. Part II reviews the developments in evolution of all ceramic systems over the last decade and considers the state of the art in several extended materials and material properties.

Dental ceramics are usually referred to as nonmetallic, inorganic structures primarily containing compounds of oxygen with one or more metallic or semi-metallic elements like aluminum, calcium, lithium, magnesium, phosphorus, potassium, silicon, sodium, zirconium & titanium [1, 10]. The term porcelain is referred to a specific compositional range of ceramic materials made by mixing kaolin, quartz and feldspar in proper proportioning and fired at high temperature [1, 10, 11]. Porcelain is essentially a white, translucent ceramic that is fired to a glazed state. [5] Dental porcelains may be classified based on their fusion temperature, microstructure, and processing technique [1, 12, 13]. According to their fusion temperature, porcelains are classified as high fusing, medium fusing, low fusing and ultra‑low fusing porcelains. The fusion temperature ranges of dental porcelains and their clinical recommendations are detailed in Table 1.

Table 1. Fusion temperature ranges of various dental porcelains and their clinical applications

2. Structure

Ceramics can appear as either crystalline or amorphous solids [1, 10] (also called glasses). Thus, ceramics can be broadly classified as non crystalline (Amorphous Solids or glasses) and Crystalline ceramics. The mechanical and optical properties of dental ceramics mainly depend on the nature and the amount of crystalline phase present. More the glassy phase more the translucency of ceramics; however, it weakens the structure by decreasing the resistance to crack propagation. On the other hand, more the crystalline phase better will be the mechanical properties which in turn would alter the aesthetics [1, 11]. Conventional or feldspathic porcelains are usually non-crystalline ceramics. These conventional porcelains are very weak and brittle in nature leading to fracture even under low stresses. Recent developments in the processing technology of dental ceramics have led to the development of crystalline porcelains with suitable fillers such as alumina, zirconia and hydroxy apatite [1, 14, 15].

2.1. Non- Crystalline Ceramics
Figure 1. Tetrahedral configuration of Silica

These are a mixture of crystalline minerals (feldspar, silica and alumina) in an amorphous (non-crystalline matrix of glass) vitreous phase. The glass-forming matrix of dental porcelains uses the basic silicone oxygen (Si-O) network with the silicon atom combining with 4 oxygen atoms, forming a tetrahedral configuration [Figure 1] in which the larger oxygen atoms serve as a matrix, with the smaller metal atoms such as silicone inserted into spaces between the oxygen atoms. Thus each silica unit consists of a single silicone atom (Si) surrounded by four oxygen atoms (O). The atomic bonds in this glass structure have both a covalent and ionic character thus making it stable and also make silica units to link with each other to form a chain configuration. Several such linked silicate unit chains form the continuous SiO4 (tetrahedral network) in glass [Figure 2]. This stable structure, with strong atomic bonds and no free electrons imparts some important qualities like excellent thermal and optical insulating characteristics, inertness translucency to the glass matrix. However, these strong dual bonds may also impart brittleness to the glass matrix leading to the fracture even at low tensile stress applications [16, 17, 18, 19].

Figure 2. Glass structure with the presence of large alkali cations
2.2. Crystalline Ceramics

Ceramics are reinforced with crystalline inclusions such as alumina and leucite into the glass matrix to form crystal glass composites as a part of strengthening the material and improving its fracture resistance (dispersion strengthening). McLean and Hughes (1965) introduced the first generation of reinforced porcelains for porcelain jacket crowns, which are generally referred to as “Aluminous porcelains” [16]. Covalent crystals are very hard and have a very high melting point, e.g. Silicone Carbide.

3. Composition

Dental ceramics are mainly composed with crystalline minerals and glass matrix. Crystalline minerals include feldspar, quartz, and alumina and perhaps kaolin as glass matrix [1, 10, 11]. The detailed composition of dental ceramics was discussed in Table 2.

Feldspar is responsible for forming the glass matrix [1]. Feldspar is the lowest melting compound and melts first on firing. Feldspar is a naturally occurring mineral and composed of two alkali aluminum silicates such as potassium aluminum silicate (K2O-Al2O3-6SiO2); also called as potash feldspar or ortho clase and soda aluminum silicate (Na2O-Al2O3-6SiO2); also called as soda feldspar or albite [1, 10, 20]. Most of the currently available porcelains contain potash feldspar as it imparts translucency to the fired restoration. Potash fuses with kaolin and quartz to form glass when heated from 1250C to 1500C [20]. Soda feldspar lowers the fusion temperature of the porcelain that results in pyroplastic flow [1, 10]. This material did not attract the porcelain manufacturers as it does not influence the translucency of the porcelain.

Quartz has high fusion temperature and provides the framework as it remains same at the firing temperature of the porcelain. Quartz also acts as filler in the porcelain restoration [1, 10, 16, 17].

Kaolin is a type of clay material which is usually obtained from igneous rock containing alumina. Kaolin acts as a binder and increases the moldability of the unfired porcelain. Kaolin also imparts opacity to the porcelain restoration so; dental porcelains are formulated with limited quantity of kaolin [21]. Glass modifiers are used as fluxes and they also lower the softening temperature and increase the fluidity [1, 17]. Color pigments or frits are added to provide the characteristic shade [1].

4. Properties

Dental ceramics exhibit excellent biocompatibility with the oral soft tissues and are also chemically inert in oral cavity. They possess excellent aesthetics. The structure of porcelain restoration is probably the most important mechanical property. The physical and mechanical properties are described in Table 3. The structure of porcelain depends upon its composition, surface integrity and presence of voids. The strength is also depends on the presence of surface ingredients. The nature, amount, particle size and coefficient of thermal expansion of crystalline phases influence the mechanical and optical properties of the materials [14]. Dental ceramics possesses very good resistance to the compressive stresses, however, they are very poor under tensile and shear stresses [1, 11, 22]. This imparts brittle nature to the ceramics [23, 24, 25] and tend to fracture under tensile stresses. Various modes of clinical fractures of ceramic structures include cracks initiating from the contact zone at the occlusal surface [25, 26], from the cementation surface beneath the contact [25, 27], and from the margins of crowns and connectors in fixed partial dentures. [28, 29, 30, 31, 32] Structural defects lead to the failure in dental ceramic prostheses. Defects may arise in the form of micro-cracks of sub-millimeter scale; during fabrication of ceramic prostheses and also from application of masticatory forces in the oral cavity [33].

Table 3. Physical and Mechanical properties of Dental Ceramics1

Fatigue strength plays an important role in the durability and longevity of dental ceramic restorations. Fatigue can be accounted for by chemically-enhanced, rate-dependent crack growth in the presence of moisture [34-41][34] and cyclic application of stresses [42-50][42]. Water enters incipient fissures and breaks down cohesive bonds holding the crack walls together and results in initiation of slow crack growth which progresses steadily over time, accelerating at higher stress levels and ultimately leading to failure [25].

Surface hardness of ceramics is very high hence they can abrade the opposing natural or artificial teeth [1, 11, 22]. Ceramics are good thermal insulators and their co-efficient of thermal expansion is almost close to the natural tooth [22, 51]. During firing any residual water is lost from the material accompanied by loss of any binders that results in volume shrinkage of about 30–40%, due to elimination of voids during sintering. Therefore, a precise control of the condensation and firing technique is required to compensate for such shrinkage value during the construction of porcelain restoration [1].

Adhesion of ceramic restoration to the natural tooth also plays a significant role in the durability of the restoration. The success of a fixed restoration depends on the use of the luting agent and cementation technique [52]. Various luting agents have been discussed in the literature [53, 54, 55]. Glass ionomer cements and resin cements are most commonly used for luting of ceramic restorations [53, 54, 56, 57]. The ceramic surface must be altered to provide adequate bonding with the luting agent and also with orthodontic bracket either by mechanical or chemical or by combined approaches [58, 59]. Mechanical approaches include use of air abrasion/sand blasting [60, 61, 62], a diamond stone bur [62, 63], sand paper disks and LASERS [64, 65, 66, 67]. However, excessive roughening of the surface should be avoided since it may induce the crack initiation and propagation within ceramic that results in fracture of the ceramic restoration during service. Chemical alteration of the ceramic surface can be introduced by either etching the surface to increase the mechanical retention of the adhesive or by changing the ceramic surface affinity to the adhesive materials [68, 69, 70, 71]. Studies have shown that chemical conditioning methods such as silanation increases the adhesion of the composite resin bond to the ceramic [72, 73, 74]. The silica of the dental ceramic is chemically united with the acrylic group of the composite resin through silanation [75]. To improve the bond strength of adhesive resins to ceramics, combination of mechanical and chemical conditioning methods are recommended [59].

5. Strengthening of Dental Ceramics

The major drawbacks of ceramics are brittleness, low fracture toughness and low tensile strength. Methods used to overcome the deficiencies of ceramics fall into two categories including methods of strengthening brittle materials and methods of designing components to minimize stress concentration and tensile stress [1, 10, 76]. Methods to strengthen the brittle materials include the development of residual compressive stress within the surface of the material and interruption of crack propagation through the material. Methods of strengthening of brittle materials are illustrated in Figure 3 [1, 10, 76, 77].

Figure 3. Methods of strengthening dental ceramics

Residual compressive stresses are introduced within the surface of glass and ceramic objects in order to gain strength. These introduced compressive stresses help in neutralizing the tensile stresses developed during service. Compressive stresses can be introduced by either of the three mechanisms such as chemical tempering, thermal tempering and thermal compatibility [1]. Chemical tempering involves replacement of smaller Na+ ions (a common constituent of variety of glasses) with the larger K+ ions. Replacement of these ions create larger residual compressive stresses (700 MPa) in the surface of the glass subjected to this treatment as the K+ ions are 35% larger than the Na+ ions. This surface compression which results in increased strength of porcelain is also called as ion exchange [1, 76, 78, 79]. Thermal tempering involves rapid cooling of the restorations’ surface from the molten state which introduces residual compressive stresses. The rapid cooling produces skin of glass surrounding soft (molten) core, which will shrink later during solidification which creates the residual tensile stress in the core and residual compressive stresses within the outer surface [1, 10, 17, 80]. Thermal compatibility method applies to porcelain fused metals. The metal and porcelain should be selected with slight mismatch in their thermal contraction coefficient. Usually the difference of 0.5 × 10–6/°C in thermal expansion between metals and porcelain causes the metal to contract slightly more than does the ceramic during cooling after firing the porcelain which results in development of residual compression in the ceramic surface [1, 10].

A dispersed crystalline phase is reinforced into the glasses or ceramics to strengthen them by interrupting the crack propagation through the material. Two different types of dispersions are used to interrupt the crack propagation such as alumina (Al2O3) or Partially Stabilized Zirconia’ (PSZ) [1, 10, 14, 76]. Al2O3 is a tough crystalline material, which can prevent the crack propagation through them and strengthen the glass [1, 10, 14, 76, 81, 82]. PSZ is capable of undergoing change in crystal structure when placed under stress and can improve the strength [1, 10, 14, 76, 83].

6. Conclusion

It is apparent that ceramics as a material group would continue to play a vital role in dentistry owing to their natural aesthetics and sovereign biocompatibility with no known adverse reactions. However, there will always remain a compromise between aesthetics and biomechanical strength. In order to achieve adequate mechanical and optical properties in the final porcelain restoration, the amount of glassy phase and crystalline phase should be optimised. Good translucency requires a higher content of the glassy phase and good strength requires a higher content of the crystalline phase. Hence, the two material phases need to be balanced. Eventhough the material is high abrasion resistant, fracture toughness and resistance to the tensile stresses are inherent disadvantages. Some attempts have been made to overcome these shortcomings. However, resistance to fracture toughness and tensile stresses is further needed to be addressed.

References

[1]  Rama Krishna Alla, Dental Materials Science, Jaypee Brothers Medical Publishers Pvt Limited, New Delhi, India, 2013, 1st Edition, 333-354.
In article      
 
[2]  Sukumaran VG, Bharadwaj N, Ceramics in Dental Applications, Trends Biomater. Artif. Organs, 20(1), 7-11, Jan 2006.
In article      
 
[3]  Hämmerle C, Sailer I, Thoma A, Hälg G, Suter A, and Ramel C, Dental Ceramics: Essential Aspects for Clinical Practice, Quintessence, Surrey, 2008.
In article      
 
[4]  Ho GW, Matinlinna JP, Insights on porcelain as a dental material. Part I: ceramic material types in dentistry, Silicon, 3(3), 109-15, July 2011.
In article      CrossRef
 
[5]  Lung CYK, Matinlinna JP, Aspects of silane coupling agents and surface conditioning in dentistry: An overview, Dent Mater, 28(5), 467-77, May 2012.
In article      CrossRefPubMed
 
[6]  Garber DA, Goldstein RE, Porcelain and Composite Inlays and Onlays: Esthetic Posterior Restorations, Quintessence, Chicago, 1994.
In article      
 
[7]  Touati B, Miara P, Nathanson D, Esthetic Dentistry and Ceramic Restorations, Martin Dunitz, London, 1999.
In article      PubMed
 
[8]  Badami V, Ahuja B, Biosmart materials: Breaking new ground in dentistry, The Scientific World J, Article ID 986912, 7 pages, Volume Feb 2014.
In article      
 
[9]  Denry I, Holloway JA, Ceramics for dental applications: A Review, Materials, 3, 351-368, Jan 2010.
In article      CrossRef
 
[10]  Anusavice KJ, Phillip’s Science of Dental Materials, Elsevier, A division of Reed Elsevier India Pvt Ltd, New Delhi, India, 2010, 11th Edition, 655-720.
In article      
 
[11]  Sakaguchi RL, Powers JM, Craig’s Restorative Dental Materials, Elsevier, Mosby, A division of Reed Elsevier India Pvt Ltd, New Delhi, India, 2007, 12th Edition, 443-464.
In article      
 
[12]  J’Obrien W, Dental Materials and their selection, 3rd edition, quintessence Publishing Co. Inc, 2002, 132-155.
In article      
 
[13]  Rashid H, The effect of surface roughness on ceramics used in dentistry: A review of literature. Eur J Dent, 8:571-9, Oct-Dec 2014.
In article      CrossRefPubMed
 
[14]  Denry IL, Recent advances in ceramics for dentistry, Crit Rev Oral Biol Med 7(2):134-143, 1996.
In article      CrossRef
 
[15]  Shenoy A, Shenoy N, Dental Ceramics: An Update, J Cons Dent, 13(4):195-203, Oct-Dec 2010.
In article      CrossRefPubMed
 
[16]  McLean JW, Hughes TH. The reinforcement of dental porcelain with ceramic oxides. Br Dent J, 119(6):251-267, Sep 1965.
In article      PubMed
 
[17]  McLean JW, The science and art of dental ceramics, Volume I: The nature of Dental Ceramics and their clinical use. Quintessence Pub Co., Chicago, 1979.
In article      
 
[18]  Claus H, Rauter H. The structure and microstructure of dental porcelain in relationship to the firing conditions. Int Prosthodont 2(4):376-384, Jui-Aug 1989.
In article      
 
[19]  van Noort R, Introduction to Dental Materials, Mosby, Spain, 1994: 201-214.
In article      
 
[20]  Lacy AM, The chmical nature of dental porcelain, Dent Clin North Am, 21(4): 661-667, Oct 1977.
In article      PubMed
 
[21]  Claus H, The structural bases of dental porcelain, Bad Sackingen, Germany: Vita Zhanfabrik, H. Rauter GmBH & Co, 1980.
In article      
 
[22]  Vallittu PK Non-metallic biomaterials for tooth repair and replacement, In Processing and bonding of dental ceramics, Woodhead Publishing Limited, Philadelphia, USA, 2013 125-160.
In article      CrossRef
 
[23]  Yoshinari M, Dérand T. Fracture strength of all-ceramic crowns. Int J Prosthodont, 7(4), 329-38, Jul-Aug 1994.
In article      PubMed
 
[24]  Sobrinho LC, Cattel MJ, Glover RH, Knowles JC, Investigation of the dry and wet fatigue properties of three all-ceramic crown systems. Int J Posthodont, 11(3), 255-62, May-Jun 1988.
In article      
 
[25]  Zhang, Sailer I, Lawn BR, Fatigue of Dental Ceramics, J Dent, 41(12): 1135-47, Dec2013.
In article      CrossRefPubMed
 
[26]  Sailer I, Gottnerb J, Kanelb S, Hammerle CH. Randomized controlled clinical trial of zirconia ceramic and metal-ceramic posterior fixed dental prostheses: a 3-year follow-up. The International Journal of Prosthodontics, 22(6):553-560, Nov-Dec 2009.
In article      PubMed
 
[27]  Kelly JR. Clinically relevant approach to failure testing of all-ceramic restorations. The Journal of Prosthetic Dentistry, 81(6):652-661, Jun 1999.
In article      CrossRef
 
[28]  Malament KA, Socransky SS. Survival of Dicor glass-ceramic dental restorations over 16 years. Part III: effect of luting agent and tooth or tooth-substitute core structure. J Prosthet Dent, 86(5): 511-519, Nov 2001.
In article      CrossRefPubMed
 
[29]  Esquivel-Upshaw JF, Young H, Jones J, Yang M, Anusavice KJ. Four-year clinical performance of a lithia disilicate-based core ceramic for posterior fixed partial dentures. The Int J Prosthodont, 21(2):155-160, Mar-Apr 2008.
In article      PubMed
 
[30]  Sax C, Hammerle CH, Sailer I. 10-year clinical outcomes of fixed dental prostheses with zirconia frameworks. Int J Computerized Dent, 14:183-202, 2011.
In article      PubMed
 
[31]  Kern M, Sasse M, Wolfart S. Ten-year outcome of three-unit fixed dental prostheses made from monolithic lithium disilicate ceramic. J Am Dent Assoc. 143(3):234-240, Mar 2012.
In article      CrossRefPubMed
 
[32]  Schmitter M, Mussotter K, Rammelsberg P, Gabbert O, Ohlmann B. Clinical performance of longspan zirconia frameworks for fixed dental prostheses: 5-year results. J Oral Rehabil. 39(7):552-557, Jul 2012.
In article      CrossRefPubMed
 
[33]  Denry I. How and when does fabrication damage adversely affect the clinical performance of ceramic restorations? Dent Mater, 29(1):85-96, Jan 2013.
In article      CrossRefPubMed
 
[34]  Morena R, Beaudreau GM, Lockwood PE, Evans AL, Fairhurst CW. Fatigue of dental ceramics in a simulated oral environment, J Dent Res. 65(7):993-997, Jul 1986.
In article      CrossRefPubMed
 
[35]  Fairhurst CW, Lockwood PE, Ringle RD, Twiggs SW. Dynamic fatigue of feldspathic porcelain. Dent Mater, 9(4):269-273, Jul 1993.
In article      CrossRef
 
[36]  White SN, Zhao XY, Zhaokun Y, Li ZC. Cyclic mechanical fatigue of a feldspathic dental porcelain. Int J Prosthodont. 8(5):413-420, Sep-Oct 1995.
In article      PubMed
 
[37]  Studart AR, Filser F, Kocher P, Gauckler LJ. In vitro lifetime of dental ceramics under cyclic loading in water. Biomater. 28(7):2695-2705, Jun 2007.
In article      CrossRefPubMed
 
[38]  Taskonak B, Griggs JA, Mecholsky JJ Jr, Yan JH. Analysis of subcritical crack growth in dental ceramics using fracture mechanics and fractography. Dent Mater. 24(5):700-707, May 2008.
In article      CrossRefPubMed
 
[39]  Gonzaga CC, Cesar PF, Miranda WG Jr, Yoshimura HN. Slow crack growth and reliability of dental ceramics. Dent Mater. 27(4):394-406, Apr 2011.
In article      CrossRefPubMed
 
[40]  Griggs JA, Alaqeel SM, Zhang Y, Miller AW 3rd, Cai Z. Effects of stress rate and calculation method on subcritical crack growth parameters deduced from constant stress-rate flexural testing. Dent Mater. 27(4):364-370, Apr 2011.
In article      CrossRefPubMed
 
[41]  Mitov G, Gessner J, Lohbauer U, Woll K, Muecklich F, Pospiech P. Subcritical crack growth behavior and life data analysis of two types of dental Y-TZP ceramics. Dent Mater, 27(7):684-691, Jul 2011.
In article      CrossRefPubMed
 
[42]  Zhang Y, Lawn BR, Rekow ED, Thompson VP. Effect of sandblasting on the long-term performance of dental ceramics. J Biomed Mater Res Part B: Applied Biomaterials. 71(2):381-386, Nov 2004.
In article      CrossRefPubMed
 
[43]  Zhang Y, Pajares A, Lawn BR. Fatigue and damage tolerance of Y-TZP ceramics in layered biomechanical systems. J Biomed Mater Res Part B: Applied Biomaterials. 71(1):166-171, Oct 2004.
In article      CrossRef
 
[44]  Bhowmick S, Zhang Y, Lawn BR. Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: bilayer structures. J Mater Res. 20(10):2792-2800, Oct 2005.
In article      CrossRef
 
[45]  Zhang Y, Bhowmick S, Lawn BR. Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: monoliths. J Mater Res. 20(8):2021-2029, Aug 2005.
In article      CrossRef
 
[46]  Zhang Y, Lawn BR. Fatigue sensitivity of Y-TZP to microscale sharp-contact flaws. J Biomed Mater Res Part B: Applied Biomaterials. 72(2):388-392, Feb 2005.
In article      CrossRefPubMed
 
[47]  Zhang Y, Song JK, Lawn BR. Deep-penetrating conical cracks in brittle layers from hydraulic cyclic contact. J Biomed Mater Res Part B: Applied Biomater. 73(1):186-193, Apr 2005.
In article      CrossRefPubMed
 
[48]  Hermann I, Bhowmick S, Zhang Y, Lawn BR. Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: trilayer structures. J Mater Res 21(2):512-521, Feb 2006.
In article      CrossRef
 
[49]  Zhang Y, Lawn BR, Malament KA, Van Thompson P, Rekow ED. Damage accumulation and fatigue life of particle-abraded ceramics. Int J Prosthodontics. 19(5):442-448, Sep-Oct 2006.
In article      PubMed
 
[50]  Bhat VS, Nandish BT, Science of Dental Materials Clinical Applications, 1st Ed., shers & Distributers, New Delhi, India, 2006, 366-387.
In article      
 
[51]  Kaminski HD, Easton AD, Dental Materials Research, Nova Science, New York, 2009: 1-21.
In article      
 
[52]  Zortuk M, Bolpaca P, Kilic K, Ozdemir E, Aguloglu S, Effects of fingure pressure applied by dentists during cementation of all-ceramic crowns, Eur J Dent, 4(4):383-388, Oct 2010.
In article      PubMed
 
[53]  Gorodovsky S, Zidan O. Retentive strength, disintegration, and marginal quality of luting cements. J Prosthet Dent 68(2):269-274, Aug 1992.
In article      CrossRef
 
[54]  Sita Ramaraju DV, Rama Krishna Alla, Venkata Ramaraju Alluri, and Raju MAKV, A Review of Conventional and Contemporary Luting Agents Used in Dentistry. American Journal of Materials Science and Engineering, 2(3): 28-35, Aug 2014.
In article      CrossRef
 
[55]  Dhillon J, Tayal SC, Tayal A, Amita, Kaur AD, Clinical aspects of adhesion of all ceramics: An Update, Ind J Dent Sci, 4(4): 123-126, Oct 2012.
In article      
 
[56]  Borges GA, Goes MF, Platt JA, Moore K, Menezes FH, Vedovato E. Extrusion shear strength between an aluminabased ceramic and three different cements. J Prosthet Dent 98(3):208-215, Sep 2007.
In article      CrossRef
 
[57]  Ravi RK, Alla RK, Shammas M, Devarhubli A, Dental Composties – A Versatile Restorative material: An Overview, Ind J Dent Sci, 5(5), 111-115, Dec 2013.
In article      
 
[58]  Urabe H, Rossouw PE, Titley KC, Yamin C, Combinations of etchants, composite resins, and bracket systems: An important choice in orthodontic bonding procedures, Angle Orthod, 69(3):267-75, Jun 1999.
In article      PubMed
 
[59]  Santos Jr. GC, Santos MJMC, Rizkalla AS, Adhesive Cementation of etchable ceramic esthetic restorations, J Cand Dent Assoc, 75(5): 379-384, Jun 2009.
In article      
 
[60]  Roulet JF, Soderholm KJ, Longmate J, Effects of treatment and storage conditions on ceramic/composite bond strength, J Dent Res, 74(1):381-7, Jan 1995.
In article      CrossRefPubMed
 
[61]  Jost-Brinkmann PG, Drost C, Can S, In-vitro study of the adhesive strengths of brackets on metals, ceramic and composite. Part 1: Bonding to precious metals and amalgam, J Orofacial Orthop, 57(2):76-87, Apr 1996.
In article      CrossRefPubMed
 
[62]  Saracoglu A, Cura C, Cotert HS, Effect of various surface treatment methods on the bond strength of the heat-pressed ceramic samples, J Oral Rehabil, 31(8):790-7, Aug 2004.
In article      CrossRefPubMed
 
[63]  Lacy AM, LaLuz J, Watanabe LG, Dellinges M, Effect of porcelain surface treatment on the bond strength to composites, J Prosthet Dent, 60(3): 288-291, Sep 1988.
In article      CrossRef
 
[64]  Ersu B, Yuzugullu B, Ruya Yazici A, Canay S, Surface roughness and bond strengths of glass infiltrated alumina ceramics prepared using various surface conditioning method, J Dent, 37(11): 848-56, Nov 2009.
In article      CrossRefPubMed
 
[65]  Guvenc Basaran, Etching enamel for orthodontics with an erbium, chromium: Yttrium-scandium-gallium-garnet laser system, Angles orthodontics, 77(1):117-123, Jan 2007.
In article      
 
[66]  Stangel I, Nathanson D, Hsu CS, Shear strength of the composite bond to etched porcelain, J Dent Res, 66(9): 1460-1465, Sep 1987.
In article      CrossRefPubMed
 
[67]  Paul P, Reddy SND, RK Alla, Rajasigamani K, Chidambaram, Evaluation of shear bond strength of stainless steel brackets bonded to ceramic crownsetched with Er; Cr: YSGG Laser and Hydrofluoric acid: An In vitro study, Brit J Medical Med Res, Accepted for publication, 2015.
In article      CrossRef
 
[68]  Rochette AL, A ceramic restoration bonded by etched enamel and resin for fractured incisors, J Prosthet Dent, 33(3): 287-293, Mar 1975.
In article      CrossRef
 
[69]  Albasheer Al Edris, Amal Al Jabr, Robert L. Cooley, Nasser Barghi, SEM evaluation of etch patterns by three etchants on three porcelains, J Prosthet Dent 64(6): 734-9, Dec 1990.
In article      CrossRef
 
[70]  Calamia JR, Viadyanathan J, Vaidyanathan TK, Hirech SM, Shear bond strength of etched porcelains, J Dent Res 64 (Supple 1):296, Mar 1985.
In article      
 
[71]  Horn HR, Porcelain laminate veneers bonded to etched enamel, Dent Clin North Am, 27(4):671-84, Oct 1983.
In article      PubMed
 
[72]  Li R, Ren Y, Han J., Effects of pulsed Nd:YAG laser irradiation on shear bond strength of composit resin bonded to porcelain surface Hua Xi Kou Qiang Yi Xue Za Zhi 18:377-9, 2000.
In article      PubMed
 
[73]  Schmage P, Nergiz I, Herrmann W, Oscan M, Influence of various surface-Conditioning methods on the bond strength of metal brackets to ceramic surfaces, Am J Ortho Dentofacial Orthop. 123(5):540-6, May 2003.
In article      CrossRef
 
[74]  Zelos L, Bevis RR, Keenan KM, Evaluation of ceramic /ceramic interfaces. Am J Orthod Dentofacial Orthop 106(1):10-21, Jul 1994.
In article      CrossRef
 
[75]  Ghassemi-Tary B, Direct bonding to porcelain: An Invitro study, Am J Orthod Dentofacial Orthop 76(1):80-83, Jul 1979.
In article      CrossRef
 
[76]  Atala MH, Gul EB, How to Strengthen Dental Ceramics. Int J Dent Sci Res, 3(1):24-27, Jan 2015.
In article      
 
[77]  Zeng K, Odén A, Rowcliffe, D. Flexure Tests on Dental Ceramics, Int J Prosthodont, 9 (5), 434-439, Sep-Oct 1996.
In article      PubMed
 
[78]  Anusavice KJ, Shen C, Lee RB. Strengthening of Feldspathic Porcelain by Ion Exchange and Tempering, J Dent Res, 71 (5), 1134-1138, May 1992.
In article      CrossRefPubMed
 
[79]  Zaimoğlu A, Can G, Fixed Prosthodontics. Ankara: Ankara University Publishing, 139-159, 2011.
In article      
 
[80]  Dehoff PH, Anusavice KJ. Tempering Stresses in Feldspathic Porcelain, J Dent Res, 68 (2), 134-138, Feb 1989.
In article      CrossRefPubMed
 
[81]  Conrad HJ, Seong WJ, Pesun, IJ. Current Ceramic Materials and Systems with Clinical Recommendations: A Systematic Review, J Prosthet Dent, 98 (5), 389-404, Nov 2007.
In article      CrossRef
 
[82]  Tinschert J, Zwez D, Marx R, Anusavice KJ. Structural reliability of alumina-, feldspar-, leucite, mica and zirconia-based ceramics. J Dent, 28(7):529-535, Sep 2000.
In article      CrossRef
 
[83]  Sundh A, Sjogren G. Fracture resistance of all-ceramic zirconia bridges with differing phase stabilizers and quality of sintering. Dent Mater 22(8):778-784, Aug 2006.
In article      CrossRefPubMed
 
  • CiteULikeCiteULike
  • MendeleyMendeley
  • StumbleUponStumbleUpon
  • Add to DeliciousDelicious
  • FacebookFacebook
  • TwitterTwitter
  • LinkedInLinkedIn