Effect of CaO Addition on the Sintering Behavior and Microstructure of Stoichiometric Spinel

Qasid A. Saleh, Baker F. Hassen

International Journal of Physics. 2017, 5(2), 57-62 doi:10.12691/ijp-5-2-5
  • Figure 1. XRD patterns of sinteredspecimens at 1200°C with different CaO content
  • Figure 2. XRD patterns of sintered specimens at 1400°C with different CaO content
  • Figure 3a. Microstructure of sintered spinel specimens at1200°C with (8 wt% CaO)
  • Figure 3b. Microstructure of sintered spinel specimens at1400°C with (8wt% CaO)
  • Figure 4. Sintered density of spinel specimens with (0-8wt% CaO) firing at 1200°C and 1400°C
  • Figure 5. Porosity of spinal samples with (0-8wt% CaO) firing at 1200°C and 1400°C
  • Figure 6. Thermal conductivity of spinel specimens with (0-8wt% CaO) firing at 1200°C and 1400°C